Supreme pour dozens of different ferrous and non-ferrous alloys. You have unlimited design flexibility with alloy choice because of the high temperature properties of ceramic moulds. Some of the most popular metal casting alloys are listed.
|
|
*Carbon steel
*Low alloy steel
*Stainless steel
*Tool steel |
*Brass
*Bronze
*Cobalt alloys
*Nickel alloys |
| |
|
|
|
|
|
|
| |
STAINLESS STEEL |
|
|
|
|
| |
Wrought |
Cast |
Tensile
strength Mpa |
0.2% Yield
strength Mpa |
%
Elongation |
Hardness
Max |
| |
303 |
CF-16F1 |
418-517 |
207-274 |
35-45 |
90Rb |
| |
304 |
CF-81 |
483-586 |
276-345 |
35-50 |
90Rb |
| |
304L |
CF-31 |
483-586 |
276-345 |
35-50 |
90Rb |
| |
309 |
CH-201 |
483-552 |
207-276 |
30-45 |
90Rb |
| |
310 |
CK-201 |
418-517 |
241-310 |
30-45 |
90Rb |
| |
316 |
CF-8M1 |
486-586 |
276-345 |
35-50 |
90Rb |
| |
316L |
CF-3M1 |
486-586 |
276-345 |
35-50 |
90Rb |
| |
410 |
CA-151 |
655-1394 |
517-1103 |
5-12 |
45Rc |
| |
416 |
IC 4161 |
655-1394 |
517-1103 |
3-8 |
45Rc |
| |
420 |
CA-401 |
1394-1551 |
896-1448 |
0-5 |
52Rc |
| |
431 |
IC 4311 |
759-1103 |
517-724 |
5-20 |
40Rc |
| |
440-C |
IC 440C1 |
- |
- |
- |
60Rc |
| |
15-5 PH |
IC 15-51 |
931-1172 |
759-1000 |
5-15 |
38Rc |
| |
17-4 PH |
IC 17-41 |
1034-1310 |
965-1103 |
6-20 |
44Rc |
| |
253MA |
C253MA2 |
600 min |
310 min |
40 min |
91Rb |
| |
2205 |
ASTM A890 4A3 |
620 min |
415 min |
25 min |
- |
| |
2507 |
ASTM A890 5A3 |
690 min |
515 min |
18 min |
- |
| |
CD4MCu |
CD4MCu1 |
931-1000 |
690-827 |
10-25 |
28-32Rc |
| |
|
|
|
|
|
|
| |
LOW ALLOY STEELS |
|
|
|
|
| |
Wrought |
Cast |
Tensile
strength Mpa |
0.2% Yield
strength Mpa |
%
Elongation |
Hardness
Max |
| |
1020 |
IC10201 |
414-483 |
207-274 |
35-45 |
90Rb |
| |
1035 |
IC10351 |
621-1034 |
276-345 |
35-50 |
90Rb |
| |
4140 |
IC41401 |
876-1394 |
276-345 |
35-50 |
90Rb |
| |
4340 |
IC43401 |
876-1394 |
207-276 |
30-45 |
90Rb |
| |
4620 |
IC46201 |
758-1034 |
241-310 |
30-45 |
90Rb |
| |
6150 |
IC61501 |
965-1394 |
276-345 |
35-50 |
90Rb |
| |
8620 |
IC86201 |
690-896 |
276-345 |
35-50 |
90Rb |
| |
8630 |
IC86301 |
827-1172 |
517-1103 |
5-12 |
45Rc |
| |
|
BS3100 A4 |
540-690 |
517-1103 |
3-8 |
45Rc |
| |
|
WCB4 |
485-655 |
896-1448 |
0-5 |
52Rc |
| |
|
|
|
|
|
|
| |
BRASS AND BRONZE |
|
|
|
|
| |
Wrought |
Cast |
Tensile
strength Mpa (min) |
0.2% Yield
strength Mpa |
%
Elongation |
|
| |
863 |
Mn Bronze HTB15 |
470 |
170 min |
18-35 |
|
| |
863 |
Mn Bronze HTB15 |
740 |
400 min |
11 min |
|
| |
864 |
Si Bronze7 |
414 |
207 min |
16 min |
|
| |
|
SCB35 |
190 |
70-100 |
11-30 |
|
| |
|
LG2 |
200 |
100-130 |
13-25 |
|
| |
|
|
|
|
|
|
| |
TOOL STEELS |
|
|
|
|
| |
Wrought |
Cast |
Annealed hardness |
Hardened Range |
|
|
| |
D2 |
CD21 |
35 Rc |
50-59 Rc |
|
|
| |
H-13 |
C H131 |
- |
44-52 Rc |
|
|
| |
|
|
|
|
|
|
| |
COBALT BASE |
|
|
|
|
| |
Wrought |
Cast |
As cast hardness |
|
|
|
| |
Stellite 6 |
Cobalt 61 |
37-45 Rc |
|
|
|
| |
HS25 |
Cobalt 251 |
20-25 Rc |
|
|
|
| |
|
|
|
|
|
|
| |
ALUMINIUM ALLOYS |
|
|
|
|
| |
Wrought |
Cast |
Tensile
strength Mpa |
0.2% Yield
strength Mpa |
%
Elongation |
|
| |
|
CC6016 |
220 min |
120 min |
5 min |
|
| |
|
DTD5008 |
216 min |
150 min |
4 min |
|
References
1 - Investment Casting Handbook
2 - Sandvik
3 - ASTM A890
4 - ASTM A216
5 - BS1400
6 - AAC Alloy
7 - UNSC 87610
|
|